By means of dimensional selection of natural lignocellulosic fibers, based on precise diameter measurements, it was recently possible to obtain fibers with relatively higher tensile strength. The present article overviews works on the statistical evaluation, through the Weibull analysis, of the ultimate tensile stress of eight lignocellulosic fibers: sisal, ramie, curaua, jute, bamboo, coir, piassava and buriti. It is shown that, for all of these fibers, the tensile strength holds an inverse relationship with the fiber diameter. Statistically this relationship conforms to a hyperbolic type of analytical equation, which discloses the possibility of unusually high strength fibers to be selected in association with very small diameters. A structural analysis using scanning electron microscopy offered an explanation to the strengthening mechanisms responsible for the superior performance of these dimensionally selected fibers.

The fibers extracted from the piassava palm tree, scientifically known as Attalea funifera, are among the stiffest lignocellulosic fibers being considered for polymer composite reinforcement. Characterization of piassava composites have been carried out for different polymeric matrices and mechanical tests. In this work the tensile properties of DGEBA/TETA epoxy matrix composites reinforced with up to 30% in volume of continuous and aligned piassava fibers were evaluated. Tensile specimens post-cured at 60ºC for 4 hours were room temperature tested and the corresponding fracture analyzed by scanning electrons microscopy. The results showed a decrease in both the tensile strength and the elastic modulus of the composites up to 30% with an increase at 40% of piassava fibers to values above those of the pure epoxy. The fracture analysis revealed a weak fiber/matrix interface, which could account for the comparative low performance of these composite in tensile tests up to 30% of volume fraction. The relatively large amount of stronger piassava fibers accounts for the better performance of the composite with 40% in volume fraction.